HIGH SPEED STEEL
COLD WORK STEELS
HOT WORK STEELS
HSS CIRCULAR SAW
FORGE- CAST PART
OTHER CUTTING TOOLS
   
 
High-speed steel Sheet/Die Steel Sheet
Specification are as follow:
Hot Rolled£º Thickness 2.5-10.5mm
                        Width 800mm
                        length 1500-2000mm
Cold Rolled£º Thickness 1.0-2.5mm
                          Width 750mm
                           length 1500-2000mm
Delivery Condition£ºBlack surface annealing HB¡Ü255

High-speed steelThe detailed material we could offer£º

    
¢Ù. W6Mo5Cr4V2 (GB), it is similar to M2( ASTM), S6-5-2(DIN), SKH51(JIS)
       Chemical Composition£º C 0.85, Si 0.38, Mn 0.35, P¡Ü0.030,         S¡Ü0.030, Cr 4.10, W 6.00, Mo 4.80 V 1.85
        Annealed Hardness: HB¡Ü255
        Heat treatment temp: Hardening 1210-1230 Temperings 550
        Secondary 63-65 HRC
       Applications£ºWidely used in all kinds of knives and durable Cold Working Die

    ¢Ú. W6Mo5Cr4V2Co5 (GB), it is similar toM35( ASTM), 1.3243(DIN), SKH35(JIS)
       Chemical Composition£º C 0.93, Si 0.38, Mn 0.35, P¡Ü0.030, S¡Ü0.030, Cr 4.10, W 6.30, Mo 4.80 V 1.85, Co 5.00
       Annealed Hardness: HB¡Ü269
       Heat treatment temp: Hardening 1200-1220 Temperings 550
       Secondary 64-67 HRC
       Applications£º This Material wear resistance, and are often used for cutting and difficult process, the faster the blade.

    ¢Û. W2Mo9Cr4VCo8 (GB), it is similar toM42 ( ASTM), 1.3247(DIN), SKH59(JIS)
        Chemical Composition£º C 1.10, Si 0.55, Mn 0.35, P¡Ü0.030, S¡Ü0.030, Cr 4.10, W 1.50, Mo 9.50 V 1.05, Co 8.00
        Annealed Hardness: HB¡Ü269
        Heat treatment temp: Hardening 1210-1230 Temperings 550
        Secondary 65-67 HRC
        Applications£º This Material wear resistance, and are often used for cutting and difficult process, the faster the blade.

   ¢Ü. W18Cr4V (GB), it is similar to T1 ( ASTM), 1.3355(DIN), SKH2(JIS)
        Chemical Composition£º C 0.75, Si 0.35, Mn 0.35, P¡Ü0.030, S¡Ü0.030, Cr 4.05, W18, V 1.10
        Applications£º Widely used in a variety of conventional tool

   ¢Ý. W9Mo3Cr4V (GB)
        Chemical Composition£º C 0.83, Si 0.35, Mn 0.35, P¡Ü0.030, S¡Ü0.030, Cr 4.05, W 8.90, Mo 2.90 V 1.45
        Annealed Hardness: HB¡Ü255
        Heat treatment temp: Hardening 1270-1285 Temperings 560
        Secondary 62-65 HRC
        Applications£º Traditional Chinese steel, and M2 similar properties, often as an alternative to the use of M2

The detailed material of Die Steel we could offer£º
    ¢Ù. Cr12Mo1V1(GB), it is similar to D2( ASTM), 1.2379(DIN), SKD11(JIS)
        Chemical Composition£º C 1.50, Si 0.35, Mn 0.35, P¡Ü0.030, S¡Ü0.030, Cr 12.10, W ¡Ü0.40, Mo 0.85 V 0.6
        Annealed Hardness: HB¡Ü255
        Heat treatment temp: Hardening 1220-1240 Temperings 550
        Secondary 63-65 HRC
        Applications£º For high-volume stamping die, Roll Die, ceramic products and cutting-blade.

    ¢Ú. Cr12MoV (GB), it is similar to1.2601(DIN), SKD11(JIS)
        Chemical Composition£º C 1.60, Si 0.35, Mn 0.35, P¡Ü0.030, S¡Ü0.030, Cr 12.00, Mo 0.50 V 0.20
        Annealed Hardness: HB¡Ü255
        Heat treatment temp: Hardening 1000-1020 Temperings 200 550
        Secondary 62-63 HRC
        Applications£º Stamping die for wear-resistant, Shenla Die, Die Ceramic Products.